2A12 Aluminum Sheet Plate

Short description:
- TEMPER: T4
- THICKNESS: 0.8-250mm (ready stock)
- WIDTH: 1250/1500/1525mm ; LENGTH: 2500/3000/3660mm
- CUTTING: Cut to size ( > 6mm thickness),
- OTHERS: Material traceability, Mass-stock,Fast shippment
Product description:
Chemical composition of 2A12 aluminum alloy
- Aluminum (Al): balance
- Silicon (Si): 0.5% max
- Ferrum (Fe): 0.5% max
- Copper (Cu): 3.8-4.9%
- Manganese (Mn): 0.3-0.9%
- Magnesium (Mg): 1.2-1.8%
- Nickel (Ni): 0.1% max
- Zinc (Zn): 0.3% max
- Titanium (Ti): 0.15% max
- Other elements: Each 0.05% max, Total 0.1% max
Typical mechanical properties of 2A12 T4 aluminum
- Tensile strength: 425MPa
- Yield strength: 275 MPa
- Elongation: 15%
- Hardness (Brinell): 130 HB
(The values are typical or min values,for reference only.)
PLACE OF ORIGIN | China |
---|---|
STANDARD | GB/T(default),ASTM,AMS,EN |
MATERIAL CERTIFICATES | Material test report, and other certificates |
SAMPLE | Support small sample (Chargeable) |
PROCESSING SERVICE | Cutting, bending, CNC, anodizing, etc. |
MOQ | Small MOQ with ready stock,even a piece. |
LOGISTICS MODE | Express, by Land,by Air,by sea |
SHIPPING PORT | Shanghai(default) |
PAYMENT OPTIONS | TT, PayPal, L/C at sight, Pay on Alibaba |
PACKAGING | Pallet(default), Wooden box(Chargeable) |
LEAD TIME | 2-7 days for ready stock.Or mutual agreement |
CUSTOMIZATION | Can be customized according to customer’s requirement |
ABOUT PRICE | Fluctuate with aluminum prices & USD exchange rate |
About 2A12 Aluminum Sheet Plate:
2A12 aluminum alloy is a high-strength aluminum alloy with good heat treatment performance, which is widely used in aerospace, military, and transportation industries. The 2A12 aluminum sheet/plate has high strength, excellent machinability, and good corrosion resistance.
The typical applications of 2A12 aluminum sheet/plate include structural parts and components of aircraft, machine parts, truck wheels, propeller components, and other high-stress structural parts.
The 2A12 aluminum sheet/plate has good weldability and can be welded by gas welding, arc welding, resistance welding, and spot welding. It can also be formed by hot and cold working, and can be forged and annealed at high temperatures.
The surface of the 2A12 aluminum sheet/plate can be treated by anodizing, polishing, brushing, sandblasting, and other methods to enhance its decorative and corrosion resistance properties. It is a reliable and cost-effective material for various applications that require high strength, good machinability, and corrosion resistance.